Shaukat Ali Lone, Dichu Xu, Richard Cook, Achim Walter Hassel,
"Effect of Chromium and Molybdenum Increment on the Crystal Structure, Nanoindentation, and Corrosion Properties of Cobalt-Based Alloys"
, in Physica Status Solidi A: Applications and Materials Science, Vol. 220, Seite(n) 2200373, 2022, ISSN: 1862-6319
Effect of Chromium and Molybdenum Increment on the Crystal Structure, Nanoindentation, and Corrosion Properties of Cobalt-Based Alloys
Sprache des Titels:
This study investigates the influence of chromium and molybdenum content (Cr: 20?35?wt%; Mo: 5 and 10?wt%) in a cobalt?chromium?molybdenum alloy system on the phases present in the microstructure, the nanomechanical, and electrochemical behavior of the alloys. A linear increase in the hardness is found in relation to the increasing chromium content for both 5 and 10?wt% Mo contents, whereas reduced modulus demonstrates an inflection at 30?wt% Cr, which is influenced by the molybdenum content. The open-circuit potential, polarization resistivity, and linear sweep voltammetry disclose that passivity of Co?Cr?Mo alloys improves in line with increasing Cr until 30?wt%, with any further increase causing a depreciation in the corrosion properties. X-Ray diffraction and optical metallographic analysis confirm that as the chromium content transitions through the 25?30?wt% range, the sigma (?) phase begins to develop within the combined matrix of hexagonal close pack martensite (?) and face-centered cubic austenite (?) phase.
Sprache der Kurzfassung:
Physica Status Solidi A: Applications and Materials Science