Christina Mitterbauer, Hrg. Gerhard Gritzner, Norbert Hörhager, Harald W. Weber,
"Yttrium-barium cuprate superconductors on titanium and rutile substrates"
: 8th European Conference on Applied Superconductivity (EUCAS 2007), Serie J. Phys.: Conf. Ser., Vol. 97, Seite(n) 012090, 2008, Yttrium-barium cuprate superconductors on titanium and rutile substrates
Christina Mitterbauer, Gerhard Gritzner, Norbert Hörhager and Harald W. Weber
J. Phys.: Conf. Ser. accepted
Original Titel:
Yttrium-barium cuprate superconductors on titanium and rutile substrates
Sprache des Titels:
Englisch
Original Buchtitel:
8th European Conference on Applied Superconductivity (EUCAS 2007)
Original Kurzfassung:
The applicability of titanium and titanium oxide as substrate material for coated
conductors was investigated. Titanium metal was rolled to a thickness of 1 mm and
mechanically polished. The surface of the titanium sheet was first oxidized at 870 °C for four
hours in flowing oxygen yielding a dense oxide layer. The oxidized surface was mechanically
polished. YBCO superconducting layers were applied to oxidized titanium and to rutile
surfaces by screen printing. The samples were then annealed in flowing oxygen at 870 °C. The
superconducting layers were characterized by X-ray diffraction, optical and electron
microscopy and by electrical and magnetic measurements. The resulting superconducting
layers were dense and showed critical temperatures of up to 92 K.
Sprache der Kurzfassung:
Deutsch
Serie:
J. Phys.: Conf. Ser.
Volume:
97
Seitenreferenz:
012090
Erscheinungsjahr:
2008
Notiz zum Zitat:
Yttrium-barium cuprate superconductors on titanium and rutile substrates
Christina Mitterbauer, Gerhard Gritzner, Norbert Hörhager and Harald W. Weber
J. Phys.: Conf. Ser. accepted