Electrically conductive bio-composites based on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and wood-derived carbon fillers
Sprache des Titels:
Englisch
Original Kurzfassung:
In this paper, biobased carbons were used as fillers in poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV). The mechanical and electrical properties of these 100% biocomposites were
analyzed. First, biocarbons were prepared from wood dust and cellulose fibers using carbonization temperatures ranging 900?2300 °C. XRD revealed significant improvements of the graphitic structure with increasing temperatures for both precursors,
with slightly higher ordering in wood-dust based carbons. An increase of the carbon content with continuous removal of other elements was
observed with increasing temperature. The carbonized cellulose fiber showed an accumulation of Na and O on the fiber surface at a carbonization temperature of 1500 °C. Significant degradation of
PHBV was observed when mixed with this specific filler, which can, most probably, be attributed to this exceptional surface chemistry. With any other fillers, the preparation of injection-molded
PHBV composites was possible without any difficulties. Small improvements in the mechanical performance were observed, with carbonized fibers being slightly superior to the wood dust analogues.
Improvements at higher filler content were observed. These effects were even more pronounced in the electrical conductivity. In the range of 15?20 vol.% carbonized fibers, the percolation
threshold could be reached, resulting in an electrical conductivity of 0.7 S/cm. For comparison, polypropylene composites were prepared using cellulose fibers carbonized at 2000 °C. Due to longer
fibers retained in the composites, percolation could be reached in the range of 5?10 vol.%. The electrical conductivity was even higher compared to that of composites using commercial carbon fibers,
showing a great potential for carbonized cellulose fibers in electrical applications.